  1. What Is Stainless Steel?
  2. When was stainless steel discovered?
  3. What is stainless steel used for?
  4. Does stainless steel corrode?
  5. What forms of corrosion can occur in stainless steels?
  6. How many types of stainless steel are there?
  7. What are the correct standards for stainless steel?
  8. Is stainless steel non-magnetic?
  9. Can I use stainless steel at low temperatures?
  10. Can I use stainless steel at high temperatures?
  11. What surface finishes are available on stainless steels?
  12. How do I choose which stainless steel to use?
  13. What is 'multiple certification'?

What surface finishes are available on stainless steels?

There are many different types of surface finish on stainless steel. Some of these originate from the mill but many are applied later during processing, for example polished, brushed, blasted, etched and coloured finishes.

The importance of surface finish in determining the corrosion resistance of the stainless steel surface cannot be overemphasised. A rough surface finish can effectively lower the corrosion resistance to that of a lower grade of stainless steel.

The European standards for stainless steels have attempted to define the most common surface finishes. However, due to the proprietary nature of many suppliers’ finishes, it is unlikely that complete standardisation is possible. This is a summary of the most common types for each product form

Common Surface Finishes for Flat Products from EN 10088-2 (for full list see Specifying finishes for stainless steel flat products (sheet and plate)

Surface Finish Code

Description

Mill finishes

 

1D

Hot rolled, heat treated, pickled. The most common hot rolled finish. A non reflective, rough surface. Not normally used for decorative applications

2B

Cold rolled, heat treated, pickled, pinch passed. The most common cold rolled mill finish. Dull grey slightly reflective finish. Can be used in this condition or frequently is the starting point for a wide range of polished finishes.

2D

Cold rolled, heat treated, pickled.

2H

Work hardened by rolling to give enhanced strength level. Various ranges of tensile or 0.2% proof strength are given in EN 10088-2 up to 1300 MPa and 1100 MPa respectively dependent on grade

2Q

Cold rolled hardened and tempered. Applies to martensitic steels which respond to this kind of heat treatment.

2R

Cold rolled and bright annealed, still commonly known as BA. A bright reflective finish. Can be used in this condition or as the starting point for polishing or other surface treatment processes e.g. colouring

 

In the following codes “1” refers to hot rolled being the starting point and “2” as cold rolled

Special Finishes

 

1G or 2G

Ground. Relatively coarse surface. Unidirectional. Grade of polishing grit or surface roughness can be specified

1J or 2J

Brushed or dull polished. Smoother than 1G/2G. Grade of polishing grit or surface roughness can be specified

1K or 2K

Satin polish. Similar to 1J/2J but with maximum specified Ra value of 0.5 micron. Usually achieved with SiC polishing belts. Alumina belts are strongly discouraged for this finish as this will have detrimental effect on corrosion resistance. Recommended for external architectural and coastal environments where bright polish (1P/2P) is not acceptable.

1P/2P

Bright polished. Non-directional, reflective. Can specify maximum surface roughness. The best surface for corrosion resistance.

2L

Coloured by chemical process to thicken the passive layer and produce interference colours. A wide range of colours is possible.

1M/2M

Patterned. One surface flat.

1S/2S

Surface coated e.g. with tin = Terne coating

2W

Corrugated. Similar to patterned but both surfaces are affected

Bead blasting

Not in EN 10088-2. Work being undertaken to more accurately define finishes.

top

Office and Postal Address: BSSA, Regus, Blades Enterprise Centre, John Street, Sheffield S2 4SW

Registered Office: Pegasus House, 463A Glossop Road, Sheffield S10 2QD

Tel: +44 (0)114 292 2636    |     Email: admin@bssa.org.uk

Copyright © 2017 British Stainless Steel Association

web design sheffield by Llama Digital